Search Jensen
[ Alloys ] [ JYE ] [ Technical Guide]


  Properties
Category Crown & Bridge
Nobility Noble
Type Type IV
Melting Range 1545°F to 1635°F
Density 12.8 g/cm3
Hardness
  Hardened
  Softened
 
280 HV
245 HV
Tensile Elongation
  Hardened
  Softened
 
10%
23%
Yield Strength
  Hardened
  Softened
 
111,000 psi
87,600 psi
Ultimate Tensile Strength
  Hardened
  Softened
 
117,000 psi
93,600 psi
Chemistry
Gold 52% Silver 24%
Copper 18% Palladium 5%
Zinc less than 1% Indium less than 1%
Iridium less than 1%    

Waxing / Spruing
Sprue to the bulkiest section.
Sprue diameter should be equal to the thickness of the bulkiest section.
Sprues longer than 3/8" should have a reservoir 1/16" from pattern.
Patterns should be no farther than 1/4" from top of investment.
Use direct method for single units and small castings.
Use indirect method for bridges and larger castings.
Investment
 Gypsum or phosphate bonded investment.
Burnout
 900°F (480°C) to 1200°F (650°C)
Melting / Casting
No extra winds of the casting arm are required (2-3 winds typical)
Multi-or single-orifice torch: 5 psi fuel and 10 psi oxygen.
The alloy will fully puddle and form a ball before it is ready to cast. DO NOT OVERHEAT.
Cast at around 1750°F (950°C).
Bench cool to obtain the hardened condition.
Water quench from a dull red heat to obtain the softened condition.
Finishing and Polishing
 Use standard techniques.
Soldering
 Recommended Solder: 615 Solder
Flux-Brown Fluoride